Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min

63

MPa

ASTM D 638

Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min

49

MPa

ASTM D 638

Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min

4

%

ASTM D 638

Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min

80

%

ASTM D 638

Tensile Modulus / 拉伸模量, 50 mm/min

3000

MPa

ASTM D 638

Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span

94

MPa

ASTM D 790

Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span

2620

MPa

ASTM D 790

Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C

550

J/m

ASTM D 256

Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C

51

J

ASTM D 3763

Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, -30°C

51

J

ASTM D 3763

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50

99

°C

ASTM D 1525

HDT（热变形温度）, 1.82 MPa, 3.2mm, unannealed （未退火）

83

°C

ASTM D 648

HDT（热变形温度）, 0.45 MPa, 6.4 mm, unannealed （未退火）

98

°C

ASTM D 648

HDT（热变形温度）, 1.82 MPa, 6.4 mm, unannealed （未退火）

90

°C

ASTM D 648

Relative Temp Index, Elec / 相对热指数， 电性能

80

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

70

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

80

°C

UL 746B

Specific Grity / 比重

1.19

–

ASTM D 792

Water Absorption / 吸水率, 24 hours

0.11

%

ASTM D 570

Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm

0.4 – 0.6

%

SABIC Method

Melt Flow Rate / 熔流率,, 260°C/2.16 kgf

21.5

g/10 min

ASTM D 1238

Volume Resistivity / 体积电阻率

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity ROA / 表面电阻率

>1.E+15

Ohm

IEC 60093

Dielectric Strength, in oil / 耐电强度，在油中, 3.2 mm

17

kV/mm

IEC 60243-1

Relative Permittivity / 相对介电常数, 50/60 Hz

2.7

–

IEC 60250

Relative Permittivity / 相对介电常数, 1 MHz

2.7

–

IEC 60250

Dissipation Factor / 耗散因素, 50/60 Hz

0.004

–

IEC 60250

Dissipation Factor / 耗散因素, 1 MHz

0.006

–

IEC 60250

UL Recognized, 94V-2 Flame Class Rating / 阻燃等级 (3)

0.75

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating / 阻燃等级 (3)

1.5

mm

UL 94

UL Recognized, 94-5VB Rating (3)

2

mm

UL 94

Drying Temperature / 干燥温度

80 – 90

°C

Drying Time / 干燥时间

3 – 4

hrs

Drying Time (Cumulative) / 干燥时间（累积的）

8

hrs

Maximum Moisture Content / 含湿量

0.04

%

Melt Temperature / 熔体温度

245 – 275

°C

Nozzle Temperature / 注嘴温度

245 – 275

°C

Front – Zone 3 Temperature / 前区3温度

245 – 275

°C

Middle – Zone 2 Temperature / 中区2温度

220 – 275

°C

Rear – Zone 1 Temperature / 后区1温度

220 – 255

°C

Mold Temperature / 模具温度

60 – 80

°C

Back Pressure / 背压

0.3 – 0.7

MPa

Screw Speed / 螺杆速度

40 – 70

rpm

Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比

30 – 80

%

Vent Depth / 排气孔深度

0.038 – 0.076

mm