Tensile Stress, yld, Type I / 抗张程度,屈服,类型I, 50 mm/min

66

MPa

ASTM D 638

Tensile Stress, brk, Type I / 抗张程度,断裂,类型I, 50 mm/min

60

MPa

ASTM D 638

Tensile Strain, yld, Type I / 拉伸伸长,屈服,类型I, 50 mm/min

4

%

ASTM D 638

Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min

98

%

ASTM D 638

Tensile Modulus / 拉伸模量, 5 mm/min

2950

MPa

ASTM D 638

Flexural Stress, yld / 挠曲强度, 屈服 , 1.3 mm/min, 50 mm span

103

MPa

ASTM D 790

Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span

2750

MPa

ASTM D 790

Tensile Stress, yield / 抗张程度,屈服, 50 mm/min

62

MPa

ISO 527

Tensile Stress, break / 抗张程度,断裂, 50 mm/min

55

MPa

ISO 527

Tensile Strain, yield / 拉伸伸长,屈服, 50 mm/min

4

%

ISO 527

Tensile Strain, break / 拉伸伸长,断裂, 50 mm/min

90

%

ISO 527

Tensile Modulus / 拉伸模量, 1 mm/min

2800

MPa

ISO 527

Flexural Stress, yield / 弯曲强度,屈服, 2 mm/min

100

MPa

ISO 178

Flexural Modulus / 挠曲模量, 2 mm/min

2500

MPa

ISO 178

Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C

625

J/m

ASTM D 256

Izod Impact, notched / 悬臂梁缺口冲击强度, -30°C

125

J/m

ASTM D 256

Instrumented IMPACT Total Energy / 装有测量仪表的落镖冲击总能量, 23°C

60

J

ASTM D 3763

Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*3 +23°C

40

kJ/m²

ISO 180/1A

Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*3 -30°C

10

kJ/m²

ISO 180/1A

Charpy（简支梁缺口冲击强度） 23°C, V-notch（V型切口） Edgew 80*10*3 sp=62mm

40

kJ/m²

ISO 179/1eA

Charpy（简支梁缺口冲击强度） -30°C, V-notch（V型切口） Edgew 80*10*3 sp=62mm

10

kJ/m²

ISO 179/1eA

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50

105

°C

ASTM D 1525

HDT（热变形温度）, 0.45 MPa, 3.2 mm, unannealed （未退火）

94

°C

ASTM D 648

HDT（热变形温度）, 1.82 MPa, 3.2mm, unannealed （未退火）

89

°C

ASTM D 648

HDT（热变形温度）, 0.45 MPa, 6.4 mm, unannealed （未退火）

102

°C

ASTM D 648

HDT（热变形温度）, 1.82 MPa, 6.4 mm, unannealed （未退火）

96

°C

ASTM D 648

CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）

6.14E-05

1/°C

ASTM E 831

CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）

5.51E-05

1/°C

ASTM E 831

Thermal Conductivity / 导热系数

0.2

W/m-°C

ISO 8302

CTE（线形膨胀系数）, -40°C to 40°C, flow（流动）

7.5E-05

1/°C

ISO 11359-2

CTE（线形膨胀系数）, -40°C to 40°C, xflow（横向）

7.5E-05

1/°C

ISO 11359-2

Ball Pressure Test, 75°C +/- 2°C

Pass

–

IEC 60695-10-2

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/50

105

°C

ISO 306

Vicat Softening Temp, Rate / 维卡软化温度，等级 B/120

105

°C

ISO 306

HDT（热变形温度）/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

90

°C

ISO 75/Af

Relative Temp Index, Elec / 相对热指数， 电性能

90

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

90

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

90

°C

UL 746B

Specific Grity / 比重

1.18

–

ASTM D 792

Mold Shrinkage / 收缩率, flow（流动）, 3.2 mm

0.4 – 0.6

%

SABIC Method

Melt Flow Rate / 熔流率,, 260°C/2.16 kgf

15.5

g/10 min

ASTM D 1238

Density / 密度

1.19

g/cm³

ISO 1183

Water Absorption / 吸水率, (23°C/sat)

0.24

%

ISO 62

Moisture Absorption / 吸水率, 平衡 (23°C / 50% RH)

0.12

%

ISO 62

Melt Volume Rate / 溶化体积流率, MVR at 260°C/2.16 kg

14

cm³/10 min

ISO 1133

Hot Wire Ignition / 热丝引燃 {PLC)

2

PLC Code

UL 746A

High Ampere Arc Ign, surface / 高电流电弧引燃，表面 {PLC}

0

PLC Code

UL 746A

Comparative Tracking Index / 相比耐漏电起痕指数 (UL) {PLC}

3

PLC Code

UL 746A

olume Resistivity / 体积电阻率

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity ROA / 表面电阻率

>1.E+15

Ohm

IEC 60093

Dielectric Strength, in oil / 耐电强度，在油中, 0.8 mm

35

kV/mm

IEC 60243-1

Dielectric Strength, in oil / 耐电强度，在油中, 1.6 mm

25

kV/mm

IEC 60243-1

Dielectric Strength, in oil / 耐电强度，在油中, 3.2 mm

17

kV/mm

IEC 60243-1

UL Recognized, 94V-1 Flame Class Rating / 阻燃等级 (3)

1.25

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating / 阻燃等级 (3)

1.5

mm

UL 94

UL Recognized, 94-5VA Rating (3)

2.5

mm

UL 94

UL Recognized, 94-5VB Rating (3)

2

mm

UL 94

Glow Wire Flammability Index / 灼热丝易燃指数 960°C, passes at

1

mm

IEC 60695-2-12

Glow Wire Ignitability Temperature / 热灯丝点火温度, 1.0 mm

800

°C

IEC 60695-2-13

Glow Wire Ignitability Temperature / 热灯丝点火温度, 3.0 mm

800

°C

IEC 60695-2-13

Drying Temperature / 干燥温度

80 – 90

°C

Drying Time / 干燥时间

3 – 4

hrs

Drying Time (Cumulative) / 干燥时间（累积的）

8

hrs

Maximum Moisture Content / 含湿量

0.04

%

Melt Temperature / 熔体温度

245 – 275

°C

Nozzle Temperature / 注嘴温度

245 – 275

°C

Front – Zone 3 Temperature / 前区3温度

245 – 275

°C

Middle – Zone 2 Temperature / 中区2温度

220 – 265

°C

Rear – Zone 1 Temperature / 后区1温度

220 – 255

°C

Mold Temperature / 模具温度

60 – 80

°C

Back Pressure / 背压

0.3 – 0.7

MPa

Screw Speed / 螺杆速度

40 – 70

rpm

Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比

30 – 80

%

Vent Depth / 排气孔深度

0.038 – 0.076

mm